Metal anticorrosion fluorine silicon coating
Metal anticorrosion fluorine silicon coating
1. Chemical composition and characteristic
The metal
anticorrosion fluorine silicon coating is made of high performance
fluorine silicone resin, IPN polymer, high quality Pigment padding and
special Auxiliary medicinal preparation, becomes through the polymer
alloy technology and the specialized coating craft preparation.
 Bearing the chemical corrosion and the electrochemistry corrosion, resisting each kind of strong corrosive medium ability;
Attaching
the strength between varnish film level, high reliability, preventing
water, oxygen and other corrosive medium destructions;
The anti- ultraviolet ray, the heat resistance change ultra, the coating maintenance lifetime is lasting for five days;
Is suitable for the poor weather condition and each kind of strong corrosion environment.
2. Range of application
Widely used
in the petroleum chemical industry, the metallurgy, the electric power,
the transportation, the ships, the mine, the building, the submarine
project, the thermal energy coal gas, the machine manufacture, the
sewage treatment and so on various domains.
It¡¯s May
take each mechanical device, the bridge, the skeleton, trough pot,
vessel, pipeline, platform and outdoors marking and so on, steel and
iron, aluminum material, stainless steel corrosion preventing coating.
3. Physical property parametric
Color and
outward appearance: each kind of color according to the color card; the
coating is toughness liquid, the varnish film is smooth.
viscosity£º ¡Ý50s / Solid content £º¡Ý55%
Fineness degree £º ¡Ü60¦Ìm / Flashing point; £º25¡æ more
Surface dry up time £º £¼1h/25¡æ
Full dry up time £º ¡Ü24h/25¡æ£¨full solidity 7days £©
Available period£º 6h/25¡æ / Hiding power£º¡Ü160g/m2
Standard film thickness £º40~60¦Ìm£¨dry film £©
4. Operation Guide
Removes
by the painting rusty stain, the old varnish film etc, the basic plane
request does not have rusts away, greasy dirt, oxide skin and so on
unreliable attachment; The steel and iron surface may use spurts sand
or pill to eliminate the rust, achieving the St3 level or the Sa2.5
level is the best; If the scene construction condition is limited,
eliminates oil rust by steel wire brush and remover processing
together; Use special-purpose cleansing agent to eliminate the old
paint level, in order to guarantee the basic plane satisfied the
construction request.
The painting
environment dose not has sand dust, sleet, mist; maintenance basic
plane clean is dry, painting under room temperature and clear weather.
using brushes spreads, spurts spreads, rolls spreads or soaks spreads
method and so on when spreads, according to the special details to
select the corresponding method.
Elects
evenly to brush spreads/Spurts spreads the primer, after waiting for
the primer table done, again paints finishes. Each painting has the
time-gap request, the list painting gap is 4 hours; If needed adjusting
the coating viscosity, select the necessary special-purpose diluents.
5. Package, Storage and transportation
This packing in the iron bucket in seal in which models; the single package is 5kg, 10kg and 20kg.
This
product should deposit in cleanly, dry, cool, ventilating place, avoids
with the acid and alkali contact, prevent the rain drenches with the
insulation exposes to the sun; the product storage time is a year.
When
transported, should add grass rope, paper box or wooden crate packing
outside the iron bucket, Avoid the force collision, prevent the leakage.
This product is flammable, strictly prohibits the smoke and fire.
Attach £º
Metal anticorrosion fluorine silicon coating technology performance chart
NO. |
Items |
Standard |
Test Method |
1 |
Adhesion ability level £© |
1 |
GB/T 1720¡ª89 |
2 |
Flexibility £¨mm£© |
1 |
GB/T 1731¡ª93 |
3 |
Hardness |
¡Ý0.4 |
GB/T 1730¡ª93 |
4 |
Impact strength£¨kg.cm£© |
¡Ý50 |
GB/T 1732¡ª93 |
5 |
Acid resistance £¨10%H2SO4£© |
Soaks 720h,Does not have bubbles, does not have falls off |
GB/T 1763¡ª89 |
£¨10%HCI£© |
Soaks 720h,Does not have bubbles, does not have falls off |
6 |
Alkali resistance £¨30%NaOH£© |
Soaks 720h,Does not have bubbles, does not have falls off |
GB/T 1763¡ª89 |
7 |
Salt water resistance
£¨3%NaCL£© |
Soaks 720h,Does not have bubbles, does not have falls off |
GB/T 1763¡ª89 |
8 |
solvent oil resistance |
Soaks 720h,Does not have bubbles, does not have falls off |
GB/T 1734¡ª93 |
9 |
Water proof |
Soaks 720h,Does not have bubbles, does not have falls off |
GB/T 1733¡ª93 |
10 |
Wet hot (soggy ) resistance |
500h£¬2 level |
GB/T 1740¡ª89 |
|